SELECTARC ALS12 TIG
Hersteller
Ceweld product
Type
Aluminium silicon alloy for welding cast aluminum parts, also suitable as brazing alloy with suitable flux.
classification
AWS
A 5.10: ER4047A
EN ISO
18273: S Al 4047A (AlSi12(A))
W.Nr.
3.2885
Anwendungen
Aluminium alloy for welding and brazing. This material is generally used for brazing aluminium sheets, for extrusions and castings. (After anodizing the weld will be of a different color)
Type
Aluminium silicon alloy for welding cast aluminum parts, also suitable as brazing alloy with suitable flux.
Anwendungen
Aluminium alloy for welding and brazing. This material is generally used for brazing aluminium sheets, for extrusions and castings. (After anodizing the weld will be of a different color)
Eigenschaften
CEWELD® AlSi12 Tig was originally developed as a brazing alloy to take advantage of its low melting point and narrow freezing range. In addition, it has a higher silicon content than AlSi5, which provides increased fluidity and reduced shrinkage. Hot cracking is significantly reduced when using AlSi12 as a filler alloy. The alloy may be used in applications at sustained elevated temperatures. Non-heat treatable. Thicker sections should be preheated (150°C) prior to welding.
Classification
AWS
A 5.10: ER4047A
EN ISO
18273: S Al 4047A (AlSi12(A))
F-nr
23
W.Nr.
3.2885
Geeignet für
G-AlSi10Mg, G-AlSi11 G-AlSi12 (Cu), G-AlSi7Mg, G-AlSi6Cu4 , G-AlSi9Mg, G-AlSi9Cu3, 4145, 3.2581, 3.2583, 3.2381, 3.2383, 3.2373, 3.2163, 3.2371, 3.2151, B 413.0, 361.0, 359.0, 356.0, 319.0, Cast aluminium
Zulassungen
CE
Schweißpositionen
Gas acc. EN ISO 14175
I1, I3
Mechanische Gütewerte
| Heat Treatment |
RP0,2 (MPa) |
Rm (MPa) |
A5 (%) |
Hardness |
|---|---|---|---|---|
| As Welded | 75 | 170 | 12 | HRc |