VAUTID Stellit 12

Hersteller
VAUTID
Ceweld product
Type
Cobalt-based thermo shock resistant alloy for overlay applications.
classification
AWS
A 5.21: ERCoCr-B
EN ISO
14700: T Co2
DIN
8555: MSG 20-GF-50-CTZ
Anwendungen
Steam-valves, high temperature liquid pumps, hot cutting tools, cutting tools for plastic, wood and paper as well as high stressed sealings and sliding surfaces.
Type
Cobalt-based thermo shock resistant alloy for overlay applications.
Anwendungen
Steam-valves, high temperature liquid pumps, hot cutting tools, cutting tools for plastic, wood and paper as well as high stressed sealings and sliding surfaces.
Eigenschaften

Outstanding alloy against abrasion, thermo-shock and corrosion combined with high temperatures. The weld deposit can be machined with tungsten tool tips and by grinding. The hardness of the weld deposit will degreas 20% at 600°C and has a nominal hardness of 49-53 HRc at room temperature. The weld deposit is high heat resistant up to 900°C. Dur 12 offers a low coefficient of friction of and exceptional resistance to galling. It has cavitation-erosion resistance ten times that of 304 stainless steel, Dur 12 can be used to protect bearing surfaces in non-lubricating conditions due to its resistance to metal-to-metal wear.

Classification
AWS
A 5.21: ERCoCr-B
EN ISO
14700: T Co2
DIN
8555: MSG 20-GF-50-CTZ
Geeignet für

46-48 HRc, Stellite 12 alloy with high temperature and abrasion resistance, thermo shock resistant and impact resistant, hardfacing valves, seats, pumps, knives, plastic recycling crushers etc.

 

Schweißpositionen
PA
PB
PC
Rücktrocknung
140°C / 24 hr
Note title
Hardness HRc
@ 20°C: 50HRc, @ 300°C: 46HRc, @600°C: 40HRc
Gas acc. EN ISO 14175
M13
Analyse
C Si Mn Cr Ni Mo V Fe W B Co Nb Cu Al Ti N
1.75 1.2 29 9 Rem.
Mechanische Gütewerte
Heat
Treatment		 RP0,2
(MPa)		 Rm
(MPa)		 A5
(%)		 Hardness
As Welded 50 HRc
Product sheet
MSDS
product sheet
Ask quotation
MSDS