Type
Submerged arc welding wire for high strength fine grain steels with >690 MPa yield strength.
classification
AWS
A 5.23: EM4~
EN ISO
26304-A: S3Ni2,5CrMo
Applications

Applications will be found in the offshore industry, shipbuilding, pressure vessels, earthmoving equipment, cranes and general structural fabrication.

Type
Submerged arc welding wire for high strength fine grain steels with >690 MPa yield strength.
Applications

Applications will be found in the offshore industry, shipbuilding, pressure vessels, earthmoving equipment, cranes and general structural fabrication.

Properties

Welding procedure (including preheat temperature, interpass temperature and PWHT) will be dependent on the base material being welded, including its thickness, and any applicable design codes. Remarkable crack resistant weld metal in combination with very low hydrogen content. Therefore, suitable for the economic processing of high-strength and low temperature fine grained structural steels. Excellent welding properties in combination with FL 155 high basic flux even in narrow gabs. To obtain optimum mechanical properties the heat input should be kept below 15 kJ/cm and interpass temperature between 100 and 150ºC.

Classification
AWS
A 5.23: EM4~
EN ISO
26304-A: S3Ni2,5CrMo
F-nr
6
FM
2
Suitable for

S690, X80, X90, X100, S690QL1, Weldox 700, Dilimax, Naxtra 70, 10CrMo9-10, 16NiCrMo12-6, high strenght steels with yield >690N/mm2, S500Q-S690Q, S500QL-S690QL, P500Q-P690Q, P500QL1-
ASTM: A514, A517. HY80, HY100, Q1(N), Oceanfit 100, Oceanfit 690

Approvals
CE, Lloyds
Welding positions
PA
PB
PC
Redrying
Not required
Analysis
C Si Mn P S Cr Ni Mo V Cu N Al Nb+Ta Ti Zr
0.09 0.2 1.6 0.01 0.01 0.3 2.1 0.6
Mechanical Properties
Heat
Treatment		 RP0,2
(MPa)		 Rm
(MPa)		 A5
(%)		 Impact Energy (J) ISO-V Hardness
-40°C -60°C
As Welded 710 780 17 80 75 HRc
Product sheet